TYPICAL PROPERTIES (1)  
MECHANICAL  Value  Unit  Standard  
Tensile Stress, yld, Type I, 50 mm/min  630  kgf/cm2  ASTM D 638  
Tensile Strain, brk, Type I, 50 mm/min  40  %  ASTM D 638  
Flexural Stress, yld, 2.6 mm/min, 100 mm span  1040  kgf/cm2  ASTM D 790  
Flexural Modulus, 2.6 mm/min, 100 mm span  27000  kgf/cm2  ASTM D 790  
Hardness, Rockwell R  123  -  ASTM D 785  
IMPACT  Value  Unit  Standard  
Izod Impact, notched, 23°C  54  cm-kgf/cm  ASTM D 256  
Izod Impact, notched, -30°C  16  cm-kgf/cm  ASTM D 256  
Instrumented Impact Total Energy, 23°C  622  cm-kgf  ASTM D 3763  
Instrumented Impact Total Energy, -30°C  553  cm-kgf  ASTM D 3763  
THERMAL  Value  Unit  Standard  
Vicat Softening Temp, Rate B/50  112  °C  ASTM D 1525  
HDT, 1.82 MPa, 3.2mm, unannealed  90  °C  ASTM D 648  
HDT, 0.45 MPa, 6.4 mm, unannealed  104  °C  ASTM D 648  
HDT, 1.82 MPa, 6.4 mm, unannealed  95  °C  ASTM D 648  
CTE, -30°C to 30°C, flow  7.2E-05  1/°C  ASTM D 696  
CTE, -30°C to 30°C, xflow  7.2E-05  1/°C  ASTM D 696  
Thermal Conductivity  0.2  W/m-°C  ASTM C 177  
Relative Temp Index, Elec  85  °C  UL 746B